Comparative of flexural strength, hardness, and fluoride release of two bioactive restorative materials with RMGI and composite resin

Aim: This study was fulfilled to evaluate the flexural strength, micro-hardness, and release of two fluoride ions of bioactive restorative materials (Cention N and Activa Bioactive), a resin modified glass ionomer (Fuji II LC), and a resin composite (Filtek z250). Methods: Forty samples from four restorative materials (Activa Bioactive, Fuji II LC, Cention N, and Filtek Z250) were provided according to the current standards of ISO 4049/2000 guide lines. Subsequently, the samples were stored for 24 hours and 6 months in artificial saliva, and successively, flexural strength and micro-hardness of the samples were measured. For each studied groups the pH was decreased from 6.8 to 4 in storage solution. The rate of changes in fluoride ion release was measured after three different storage periods of 24 hours, 48 hours, and 6 months in distilled water, according to the previous studies' method. Two-way ANOVA, One-way ANOVA, Tukey HSD Pair wise comparisons, and independent t-tests were used to analyze data (α= 0.05). Results: The highest flexural strength and surface micro-hardness after 24 hours and also after 6 month were observed for Cention N(p<0.001).Flexural strength of all samples stored for 6 months was significantly lower than the samples stored for 24 hours(p<0.001). The accumulative amount of the released fluoride ion in RMGI, after six-month storage period in distilled water was considerably higher (p<0.001) than 24 hours and 48 hours storage. The amount of fluoride ion release with increasing acidity of the environment (from pH 6.8 to 4) in Fuji II LC glass ionomer was higher than the bioactive materials (p<0.05). Conclusion: The flexural strength of RMGI was increased after storage against the Activa Bioactive,Cention N and Z250 composite. Storage of restorative materials in artificial saliva leads to a significant reduction in micro hardness. The behavior and amount of released fluoride ions in these restorative materials, which are stored in an acidic environment, were dependent on the type of restorative material

Influence of laser deproteinization of acid-etched dentin on marginal microleakage of class V composite restoration

Aim: Recent reports indicate that deproteinization of acid-etched dentin surface can extend penetration depth of adhesive agents. The main goal of the present research was to investigate the deproteinization effect of Nd:YAG and diode 940 lasers on acid-etched dentin and microleakage grade in class V composite restorations. Methods: 36 extracted human premolar teeth were selected to make standard buccal and lingual class V cavities. These samples were randomly split into three sub-groups: 1.Control group, in which composite was applied for restoration after etch and bonding process without deproteinization; 2.Nd:YAG laser group, in which the teeth were deproteinized with Nd:YAG laser after etching and painting internal surfaces of cavities with Van Geison stain and then composite restorations applied just as control group; 3.Diode laser group, in which the process was similar to Nd:YAG laser group, but instead, diode 940 laser was irradiated. The teeth were bisected into two equal longitudinal buccal and lingual halves. Marginal microleakage of samples was scored by using a stereomicroscope. Kruskal- Wallis, Mann-Whitney U and Fisher's statistical tests were employed for analysis of the obtained data. Results: A significant reduction in marginal microleakage was observed for both groups treated with laser (Nd:YAG and diode 940)compared to control (p=0.001 & p=0.047). There was no significant difference in marginal microleakage between Nd:YAG laser and diode 940groups (P = 0.333). Conclusion: Nd:YAG and diode 940 laser deproteinization of acid-etched dentin decreased the marginal microleakage of in-vitro class V resin composite restorations

Effect of proteolytic agents on microleakage of etch and rinse adhesive systems

Objective: this study aimed to assess the effect of treatment of phosphoric acid etched dentin surface with 5% bromelain enzyme and Nd:YAG laser prior to the use of etch and rinse adhesive systems on microleakage margins of class V composite restorations. Materials and Methods: sixty sound premolar teeth were selected. Standard class V cavities were prepared in the buccal and lingual surfaces of each teeth. Preparation in that way 1 mm of the cavity was above and 1 mm of it was below the cementoenamel junction. The teeth were then randomly divided into three groups including 20 teeth(40cavities in each gorup). Two ethanol base etch and rinse system (Adper Single Bond and OptiBond Solo) was applied in each group. In the control group, cavities were etched with 37% phosphoric acid. Adper Single Bond was applied to 20 and OptiBond Solo was applied to the remaining 20 cavities and they were restored with Z250 composite (n=40). The same procedures were performed in bromelain and Nd:YAG laser groups with the difference that prior to the application of adhesive, aqueous 5% bromelain was applied in bromelain group while Nd:YAG laser was irradiated in laser group. All teeth were thermocycled and their apices were sealed with sticky wax. The tooth surfaces were coated with nail varnish except for 1 mm around the restoration margins, and the teeth were then immersed in fuchsine and sectioned by a diamond disc into mesial and distal halves. Marginal microleakage at both sides was determined and scored under a stereomicroscope at x40 magnification. Then data were analyzed using the Kruskal Wallis and Mann Whitney tests (α=0.05). Results: according the result of Mann Whitney test, Cervical margins showed significantly higher microleakage than the occlusal margins (P=0.000) but no significant difference was noted in microleakage of occlusal (P=0.362) or gingival (P=0.147) margins among the three groups by Kruskal Wallis test. Conclusion: in conclusion, application of proteolytic agents(5% bromelain solution and Nd:YAG laser) on acid-etched dentin surface prior to the application of adhesive has no significant effect on marginal microleakage of class V composite restorations (AU)